以2,6-二氨基吡啶、均苯三甲酰氯为水相和油相单体,通过界面聚合法制备吡啶功能化聚酰胺(PA-PY)膜,随后利用酰氯水解羧基和吡啶氮原子与锌离子的配位作用,在膜表面原位生长ZIF-8(类沸石咪唑酯骨架材料-8),制备了ZIF-8/聚酰胺(ZIF-8/PA-PY)双层复合纳滤膜。扫描电镜分析结果表明:原位生长法可在PA-PY分离层生成晶型结构完整、致密的ZIF-8层,且随着原位生长时间的增加,ZIF-8层逐渐增厚。ZIF-8/PA-PY双层复合纳滤膜对负电性染料的截留率较高,原位生长时间为12h时,双层复合纳滤膜对甲基蓝截留率为97.9%,刚果红为99.6%。
The pyridine functionalized polyamide (PA-PY) membrane was prepared by interfacial polymerization using 2,6-diaminopyridine as aqueous monomers and trimesoyl chloride as organic phase monomers.Next,the carboxyl group and the pyridine nitrogen atom on the surface of the PA-PY membrane were used to coordinate with the zinc ion.ZIF-8 was grown in-situ on the surface of the membrane to prepare a ZIF-8/PY double-layer composite nanofiltration membrane.The results of SEM showed ZIF-8 layer with complete crystal structure could be generated by in-situ growth method on the surface of PA-PY membrane,and the ZIF-8 layer gradually thickened with the increase of in-situ growth time.ZIF-8/PA-PY double-layer membrane had higher rejection rate for negatively charged dyes.When the in-situ growth time was 12h,the membrane had a methyl blue rejection rate of 97.9% and congo red of 99.6%,respectively.
[1] Shannon M A,Bohn P W,Elimelech M,et al.Science and technology for water purification in the coming decades[J].Nature,2008,452(7185):301-310.
[2] 李新冬,代武川,袁佳彬,等.纳滤膜分离技术处理饮用水研究进展[J].应用化工,2018,47(8):217-221.
[3] Zhu J,Qin L,Uliana A,et al.Elevated performance of thin film nanocomposite membranes enabled by modified hydrophilic MOFs for nanofiltration[J].ACS Applied Materials & Interfaces,2017,9(2):1975-1986.
[4] 李丹,江晖,廖天宇,等.乙二胺改性ZIF-8的制备及其水体中As(Ⅲ)和As(Ⅴ)的吸附研究[J].化工新型材料,2017,45(5):130-133.
[5] Buragohain A,Couck S,Van Der Voort P,et al.Synthesis,characterization and sorption properties of functionalized Cr-MIL-101-X(X=—F,—Cl,—Br,—CH3,—C6H4,—F2,—(CH3)2) materials[J].Journal of Solid State Chemistry,2016,238:195-202.
[6] Lai Z.Development of ZIF-8 membranes:opportunities and challenges for commercial applications[J].Current Opinion in Chemical Engineering,2018,20:78-85.
[7] Sorribas S,Gorgojo P,Téllez C,et al.High flux thin film nanocomposite membranes based on metal-organic frameworks for organic solvent nanofiltration[J].Journal of the American Chemical Society,2013,135(40):15201-15208.
[8] Lee T H,Oh J Y,Hong S P,et al.ZIF-8 particle size effects on reverse osmosis performance of polyamide thin-film nanocomposite membranes:importance of particle deposition[J].Journal of Membrane Science,2019,570:23-33.
[9] Zhao W,Liu H,Meng N,et al.Graphene oxide incorporated thin film nanocomposite membrane at low concentration monomers[J].Journal of Membrane Science,2018,565:380-389.
[10] Guo X,Liu Q,Liu J,et al.Magnetic metal-organic frameworks/carbon dots as a multifunctional platform for detection and removal of uranium[J].Applied Surface Science,2019,491:640-649.
[11] Zhang H,Zhao M,Yang Y,et al.Hydrolysis and condensation of ZIF-8 in water[J].Microporous and Mesoporous Materials,2019,288:109568.
[12] Chiang Y C,Hsub Y Z,Ruaan R C,et al.Nanofiltration membranes synthesized from hyperbranched polyethyleneimine[J].Journal of Membrane Science,2009,326(1):19-26.
[13] Spólnik P,Stopa B,Piekarska B,et al.The use of rigid,fibrillar congo red nanostructures for scaffolding protein assemblies and inducing the formation of amyloid-like arrangement of molecules[J].Chemical Biology & Drug Design,2007,70(6):491-501.
基金资助
国家自然科学基金(21576114)
PDF